Manufacturer > Loctite

LOCTITE 2701/10ML – High Strength Threadlock

Part Number: LOCTITE 2701/10ML
Race Category
ALL
Circuit
Karting
Offroad
Sprint
Product Category
Adhesives & Abrasives

Loctite 2701/10ml – High Strength Threadlock

Loctite 2701 High strength, especially for chromated surfaces Threadlocker.

Loctite 2701 is designed for the permanent locking and sealing of threaded fasteners. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. This product is particularly suited for use on inactive substrates and/or where maximum resistance to hot oil is required.

Product Description

Technology: Acrylic
Chemical Type: Dimethacrylate ester
Appearance (uncured): Green liquid
Fluorescence: Positive under UV light
Components: One component: Requires no mixing
Viscosity: Low
Cure: Anaerobic
Secondary Cure: Activator
Application: Threadlocking
Strength: High

Typical Curing Performance

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph shown in the data sheet shows the shear strength developed with time on steel pins and collars compared to different materials and tested according to ISO 10123.

Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The graph shown in the data sheet shows shear strength developed with time on steel pins and collars at different controlled gaps and tested according to ISO 10123.

Cure Speed vs. Temperature
The rate of cure will depend on the temperature. The graph shown in the data sheet shows the shear strength developed with time at different temperatures on steel pins and collars and tested according to ISO 10123.

Cure Speed vs. Activator
Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph shown in the data sheet shows the shear strength developed with time on zinc dichromate steel pins and collars using and tested according to ISO 10123.

Typical Properties of Uncured Material
Specific Gravity @ 25 °C 1.08
Viscosity, Brookfield – RVT, 25 °C, mPa·s (cP):
–Spindle 2, speed 20 rpm: 500 to 900

Typical Performance of Cured Material
Adhesive Properties:

After 24 hours @ 22 °C
Breakaway Torque, ISO 10964:
M10 black oxide steel nuts and bolts: N·m 26 to 50 (lb.in.) (230 to 440)
Prevail Torque, ISO 10964:
M10 black oxide steel nuts and bolts: N·m ≥15 (lb.in.) (≥132)

Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 black oxide steel nuts and bolts: N·m 30 to 60 (lb.in.) (265 to 530)

Max. Prevail Torque, ISO 10964, Pre-torqued to 5 N·m:
M10 black oxide steel N·m 36 to 60 nuts and bolts: (lb.in.) (320 to 530)

Compressive Shear Strength, ISO 10123:
Steel pins and collars: N/mm² 18 to 30: (psi) (2,610 to 4,350)

Storage
Please store this product in the unopened container in a dry location.
Further storage information may be indicated on the product container labeling.

General information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.

Not sure if this product is right for you?
If you are not sure if this product is right for your requirements, please contact our friendly sales team and they will be able to help you.

  • Pack sizes: 10ml 50ml 250ml
  • Service temperature range: -55°C - +150°C
  • Strength: High
  • Maximum thread size: Up to M20
  • Fixture time steel: 10 min
  • Fixture time brass: 4 min.
  • Fixture time stainless steel: 25 min.
  • Breakaway torque M10 bolts: 38Nm

£6.03Each (exc VAT)