Loctite 3090/10G – Cyanoacrylate 2k Superglue

Loctite 3090 is a two component, fast curing, gap filling adhesive with excellent bonding characteristics to a variety of substrates including plastics, rubbers and metals. Loctite 3090 is designed for the assembly of parts with varying or undefined bond gaps up to 5 mm (0.2 in), or for applications where complete cure of excess adhesive is a requirement. The gel consistency prevents adhesive flow even on vertical surfaces. Loctite 3090 is also suited for bonding porous materials such as wood, paper, leather and fabric.

Product Description

Technology: Cyanoacrylate
Chemical Type: Ethyl cyanoacrylate
Appearance (Comp. A): Clear to slightly cloudy gel
Appearance (Comp. B): Transparent colorless liquid
Appearance (Mixture): Clear to slightly cloudy gel
Components: Two component – requires mixing
Viscosity: Thixotropic gel
Cure: Two component cure after mixing
Application: Bonding

Typical Properties of Uncured Material
Part A:
Specific Gravity @ 25°C: 1.1
Casson Viscosity, 25°C, mPa·s (cP):
Cone and Plate Rheometer: 150 to 450

Part B:
Casson Viscosity, 25°C, mPa·s (cP):
Cone and Plate Rheometer: 10 to 30

Mixed:
Open Time @ 25°C, seconds: 90 to 180

Typical Curing Performance

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph shown in data sheet shows the shear strength developed with time on steel lap shears compared to different materials and tested according to ISO 4587.

Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The graph shown in data sheet shows the shear strength developed with time on Polycarbonate lap shears at different controlled gaps and tested according to ISO 4587.

Cure Speed vs. Temperature
The rate of cure will depend on the ambient temperature. The graph shown in data sheet shows the shear strength developed with time at different temperatures on Polycarbonate lap shears and tested according to ISO 4587.

Typical Performance of Cured Material

Cured for 1 week @ 22°C
Physical Properties:
Glass Transition Temperature ISO 11359-2, °C: 116
Shore Hardness, ISO 868, Durometer D: 79
Tensile Strength, at break, ISO 527-3: N/mm² 28 (psi) (4,060)
Tensile Strength, at yield, ISO 527-3: N/mm² 28 (psi) (4,060)
Tensile Modulus, ISO 527-3: N/mm² 1,870 (psi) (271,150)
Elongation, at break, ISO 527-3, %: 2.5
Elongation, at yield, ISO 527-3, %: 2.5
Coefficient of Thermal Expansion, ISO 11359-2, K-1: 110×10-6
Coefficient of Thermal Conductivity, ISO 8302, W/(m·K): 0.35

Storage
Please store this product in the unopened container in a dry location.
Further storage information may be indicated on the product container labeling.

Optimal Storage: 8°C to 21°C. Storage below 8°C or greater than 28°C can adversely affect product properties.

General information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.

Not sure if this product is right for you?
If you are not sure if this battery is right for your requirements, please contact our friendly sales team and they will be able to help you.

£15.27Each (exc VAT)

In Stock