Loctite 326/50ml – Magnet Bonding

Loctite AA 326 structural bonding – magnet bonder

Loctite AA 326 typical applications include bonding ferrites to plated materials in electric motors, loudspeaker hardware and jewelry where fast fixturing is required.

Product Description

Technology: Acrylic
Chemical Type: Polyurethane methacrylate
Appearance: (uncured) Transparent, yellow to light amber liquid
Components: One component – requires no mixing
Viscosity: High
Cure: Anaerobic with activator
Cure Benefit: Room temperature cure
Application: Bonding

Typical Properties of Uncured Material
Specific Gravity @ 25°C: 1.1
Viscosity, Brookfield – RVT, 25 °C, mPa·s (cP):
–Spindle 6, speed 20 rpm: 14,000 to 22,000
Viscosity, EN 12092 – MV, 25 °C, after 180 s, mPa·s (cP):
Shear rate 36: 10,000 to 20,000

Mixed:
Open Time @ 25°C, seconds: 90 to 180

Typical Curing Performance

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph shown in the data sheet shows the shear strength developed with time on grit blasted steel lap shears compared to different materials and tested according to ISO 4587. (Activator 7649 applied to one surface).

Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The graph shown in the data sheet shows shear strength developed with time on grit blasted steel lap shears at different controlled gaps and tested according to ISO 4587. (Activator 7649™ applied to one surface)

Cure Speed vs. Temperature
The rate of cure will depend on the ambient temperature. The graph shown in the data sheet shows shear strength developed with time at 120°C on grit blasted steel lap shears and tested according to ISO 4587.

Typical Performance of Cured Material

After 24 hours @ 22°C, Activator 7649 on 1 side
Lap Shear Strength, ISO 4587:
Steel (grit blasted): N/mm² ≥15.2 (psi) (2,200)

Tensile Strength, ISO 6922:
Steel (grit blasted): N/mm² 24 (psi) (3,500)

After 24 hours @ 22°C, Activator 7649™ on 2 sides
Lap Shear Strength, ISO 4587:

Steel (grit blasted) :
0.25 mm gap: N/mm² ≥13.8 (psi) (2,000)

Storage
Please store this product in the unopened container in a dry location.
Further storage information may be indicated on the product container labeling.

General information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.