LOCTITE 3295/50ML – Multi Bond

Loctite 3295/50ml – Multi Bond

Loctite AA 3295 structural bonding – general purpose

Loctite AA 3295 is a two component toughened acrylic adhesive system for high strength structural bonding. The two components are applied premixed from a static mixer which cures rapidly on assembly of the joint.

Product Description

Technology: Acrylic
Chemical Type: Methacrylate
Appearance, Resin (Component A): Yellow liquid
Appearance, Hardener (Component B): Blue liquid
Appearance (Mixture): Green
Components: Two component – requires mixing
Cure: Room temperature cure after mixing
Application: Bonding
Specific Benefit: Suitable for a wide range of substrates, including metals and plastics

Typical Properties of Uncured Material
Specific Gravity @ 25°C: 1.02
Viscosity, Brookfield – RVT, 25°C, mPa·s (cP):
–Spindle 6, speed 20 rpm: 15,000 to 38,000

Typical Curing Performance

Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph below shows the shear strength developed with time on steel lap shears compared to different materials and tested according to ISO 4587.

Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The following graph shows the shear strength developed with time on steel lap shears at different controlled gaps and tested according to ISO 4587.

Cure Speed vs. Temperature
The rate of cure will depend on the ambient temperature. The graph below shows the shear strength developed with time at different temperatures on steel lap shears and tested according to ISO 4587.

Typical Performance of Cured Material

Cured for 48 hours @ 22°C
Lap Shear Strength, ISO 4587:
Steel: N/mm² 24.8 (psi) (3,600)
Oiled steel: N/mm² 7.6 (psi) (1,100)
Aluminum: N/mm² 17.3 (psi) (2,500)
ABS: N/mm² 2.1 (psi) (300)
PVC: N/mm² 4.5 (psi) (650)
Polycarbonate: N/mm² 2.8 (psi) (400)
Wood: N/mm² 2.8 (psi) (400)

“T” Peel Strength, ISO 11339:
Aluminum: N/mm 3.5 (lb/in) (20)

Storage
Please store this product in the unopened container in a dry location.
Further storage information may be indicated on the product container labeling.

General information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for chlorine or other strong oxidizing materials.